PENGARUH PELAKUAN PANAS ISOTHERMAL ANNEALING BAJA KARBON MENENGAH TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO

Akram, Fadhal (2021) PENGARUH PELAKUAN PANAS ISOTHERMAL ANNEALING BAJA KARBON MENENGAH TERHADAP SIFAT MEKANIK DAN STRUKTUR MIKRO. S-1 thesis, 021008 Universitas Tridinanti Palembang.

[img] Text (Bab 1)
Bab 1.pdf - Published Version

Download (772kB)
[img] Text (Bab 2)
BAB II.pdf - Published Version
Restricted to Repository staff only

Download (522kB) | Request a copy
[img] Text (Bab 3)
BAB III.pdf - Published Version
Restricted to Repository staff only

Download (312kB) | Request a copy
[img] Text (Bab 4)
BAB IV.pdf - Published Version
Restricted to Repository staff only

Download (723kB) | Request a copy
[img] Text (Bab 5)
Bab 5.pdf - Published Version
Restricted to Repository staff only

Download (520kB) | Request a copy

Abstract

ABSTRAK Dalam Penggunaan material logam sangatlah penting dalam mengetahui sifat mekanik dari suatu material logam, karena dengan kebutuhan pemakaian. Dalam pelaksanaan proses austenisasi temperatur yang digunakan adalah 835℃, 845℃ dan 855℃ dengan waktu tahan 10 menit. Pengujian kekerasan dan stuktur mikro terhadap baja karbon menengah AISI 1045 yang dilakukan bertujuan untuk mengetahui pengaruh proses perlakuan panas terhadap nilai kekerasan, besar butir dan struktur mikro yang terjadi pada benda uji pada temperatur austenisasi. Dari hasil pengujian dapat diketahui bahwa dengan di lakukan perlakuan panas pada temperatur austenisasi benda uji mengalami penurunan nilai kekerasan. Kata Kunci : Baja, Kekerasan, Struktur Mikro

Item Type: Thesis (S-1)
Subjects: T Technology > TJ Mechanical engineering and machinery
Divisions: Fakultas Teknik > S1 Teknik Mesin
Depositing User: Tn Fadhal Akram
Date Deposited: 10 May 2021 01:37
Last Modified: 10 May 2021 01:37
URI: http://repository.univ-tridinanti.ac.id/id/eprint/2393

Actions (login required)

View Item View Item