PENGARUH PERLAKUAN PANAS HARDENING YANG DILANJUTKAN DENGAN TEMPERING MENGGUNAKAN MEDIA PENDINGINAN OLI DAN AIR ES PADA MATERIAL AISI 1037

Lubis, Putra Ramadoni (2025) PENGARUH PERLAKUAN PANAS HARDENING YANG DILANJUTKAN DENGAN TEMPERING MENGGUNAKAN MEDIA PENDINGINAN OLI DAN AIR ES PADA MATERIAL AISI 1037. S-1 thesis, 021008 Universitas Tridinanti.

	Text (BAB I) Bab 1 doni-1.pdf Download (512kB)
	Text (BAB II) bab 2 doni.pdf Restricted to Repository staff only Download (224kB) | Request a copy
	Text (BAB III) bab 3 doni.pdf Restricted to Repository staff only Download (119kB) | Request a copy
	Text (BAB IV) bab 4 doni.pdf Restricted to Repository staff only Download (520kB) | Request a copy
	Text (BAB V) bab 5 doni.pdf Restricted to Repository staff only Download (59kB) | Request a copy

Abstract

ABSTRAK Penelitian ini bertujuan untuk menyelidiki pengaruh proses perlakuan panas hardening yang dilanjutkan tempering terhadap kekerasan dan struktur mikro pada AISI 1037. AISI 1037 merupakan baja karbon menengah yang cukup sering digunakan pada pembuatan perkakas, roda gigi, dan konstruksi lainnya. Dalam penelitian ini dilakukan dua proses perlakuan panas, yaitu hardening pada suhu 825ºC dan tempering pada suhu 500ºC dengan media pendingin oli dan air es. Setelah proses perlakuan panas, dilakukan uji kekerasan dengan metode rockwell serta pengamatan struktur mikto menggunakan mikroskop optik. Hasil penelitian ini menunjukkan perlakuan hardening tanpa media pendingin memiliki kekerasan rata-rata 80,1 HRB. perlakuan hardening menggunakan media pendingin air es mendapatkan kekerasan rata-ratanya 90,1 HRB dan mengalami perubahan menjadi 82,4 HRB setelah dilanjutkan tempering. Perlakuan hardening menggunakan media pendingin oli SAE 20-50 akan menurunkan kekerasan rata-rata material menjadi 79,8 HRB dan mengalami perubahan menjadi 81,9 HRB setelah dilanjutkan tempering. Kesimpulannya, perlakuan panas hardening dan tempering secara efektif mengubah kekerasan dan memperbaiki struktur mikro AISI 1037, dengan hardening menggunakan media pendingin oli dan air es akan menghasilkan struktur mikro yang lebih seragam yaitu martensite. Proses tempering menggunakan media pendingin udara akan mengubah struktur mikro dengan butiran ferrite dan pearlite yang lebih halus. Kata Kunci: AISI 1037, hardening, tempering. ABSTRACT The study was to investigate the effects of the hardening process that continued tempering and microstructure on the AISI 1037. AISI 1037 is medium steel that is used quite frequently in toolmaking, gear, and other construction. In the study, hardening at 825ºC variants and at 500ºC temperers was conducted with oil - cooling, water-cooled media. After the heat treatment process, rockwell's methods of violence and the observation of the mikto structure were used under an optical microscope. The research results that hardening works without cooling media were subject to an average of 80,1 human resources. Hardening treatment of air- cooling media was found in excess of 90,1 HRB on the average and increased to 82.4 HRB after tempering. Hardening treatment using sold-cooling machines from 20 - 50 will reduce the average material violence to 79,8 HRB and change to 81,9 HRB after tempering. In conclusion, the treatment of hardening and tempering effectively alters violence and improve the microstructure of AISI 1037. Hardening using oil - cooling media and putting ice in place will result in a more uniform microstructure called martensite. Tempering uses air-cooled media will change micro-structures with more refined ferrite beads and pearlites. Keyword: AISI 1037, hardening, tempering

Item Type:	Thesis (S-1)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Depositing User:	Tn Putra Ramadoni Lubis
Date Deposited:	26 Feb 2025 02:57
Last Modified:	26 Feb 2025 02:57
URI:	http://repository.univ-tridinanti.ac.id/id/eprint/9882

Actions (login required)

View Item