STUDI KEKERASAN SAMBUNGAN LAS SMAW (SHIELDING METAL ARC WELDING) PADA BAJA AISI 1040 TERHADAP BENTUK KAMPUH V, I, DAN U

Ramadhan, Andika (2025) STUDI KEKERASAN SAMBUNGAN LAS SMAW (SHIELDING METAL ARC WELDING) PADA BAJA AISI 1040 TERHADAP BENTUK KAMPUH V, I, DAN U. S-1 thesis, 021008 Universitas Tridinanti.

	Text (BAB I) bab 1 andika_compressed.pdf Download (851kB)
	Text (BAB II) bab 2 andika.pdf Restricted to Repository staff only Download (495kB) | Request a copy
	Text (BAB III) bab 3 andika.pdf Restricted to Repository staff only Download (608kB) | Request a copy
	Text (BAB IV) bab 4 andika.pdf Restricted to Repository staff only Download (1MB) | Request a copy
	Text (BAB V) bab 5 andika.pdf Restricted to Repository staff only Download (392kB) | Request a copy

Abstract

ABSTRAK Pengelasan SMAW (Shielding Metal Arc Welding) adalah proses yang memanfaatkan panas dari busur listrik untuk mencairkan logam dasar dan elektroda, sehingga menghasilkan sambungan yang kuat. Penelitian ini bertujuan untuk menganalisis hasil sambungan las SMAW dengan variasi kampuh V, I, dan U pada baja karbon AISI 1040, dengan kuat arus pengelasan 95 A dan elektroda E7018 berdiameter 3,2 mm. Baja AISI 1040, yang memiliki kadar karbon 0,37% - 0,42%, mengalami perubahan termal yang signifikan selama proses pengelasan, mempengaruhi sifat mekanik dan struktur mikro pada daerah HAZ (Heat Affected Zone). Hasil penelitian menunjukkan bahwa nilai kekerasan pada benda asal adalah 84,7 HRB, sedangkan logam isian hampir setara dengan benda asal. Namun, nilai kekerasan di daerah HAZ mengalami penurunan akibat pengaruh pendinginan yang tidak merata, yang menyebabkan butiran menjadi kasar. Sebaliknya, pada logam dasar, peningkatan kekerasan terjadi karena proses persiapan menggunakan gerinda tangan dan pemotongan laser. Struktur mikro yang diperoleh terdiri dari pearlit dan ferrit, dengan kemungkinan terbentuknya martensite akibat komposisi kimia yang mendukung. Kata Kunci : Pengelasan SMAW, Baja Karbon AISI 1040, Kampuh las V, I dan U ABSTRACT SMAW (Shielding Metal Arc Welding) is a process that utilizes heat from an electric arc to melt the base metal and electrode, resulting in a strong joint. This study aims to analyze the results of SMAW welding joints with variations of V, I, and U welds on AISI 1040 carbon steel, with a welding current of 95 A and an E7018 electrode with a diameter of 3.2 mm. AISI 1040 steel, which has a carbon content of 0.37% - 0.42%, undergoes significant thermal changes during the welding process, affecting the mechanical properties and microstructure in the HAZ (Heat Affected Zone) area. The results showed that the hardness value of the original object was 84.7 HRB, while the filler metal was almost equivalent to the original object. However, the hardness value in the HAZ area decreased due to the influence of uneven cooling, which caused the grains to become coarse. Conversely, in the base metal, the increase in hardness occurred due to the preparation process using a hand grinder and laser cutting. The microstructure obtained consists of pearlite and ferrite, with the possibility of martensite formation due to the supporting chemical composition. Keywords: SMAW Welding, AISI 1040 Carbon Steel, Weld Welds V, I and U

Item Type:	Thesis (S-1)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Depositing User:	Tn Andika Ramadhan
Date Deposited:	12 Jun 2025 04:51
Last Modified:	12 Jun 2025 04:51
URI:	http://repository.univ-tridinanti.ac.id/id/eprint/9991

Actions (login required)

View Item