ANALISA PERUBAHAN SIFAT KEKERASAN TERHADAP VARIASI TEMPERATUR HARDENING PADA BAJA HQ 760

VIYOGA, ALDI (2021) ANALISA PERUBAHAN SIFAT KEKERASAN TERHADAP VARIASI TEMPERATUR HARDENING PADA BAJA HQ 760. S-1 thesis, 021008 Universitas Tridinanti Palembang.

	Text (Bab 1) BAB I.pdf - Published Version Download (1MB)
	Text (Bab 2) BAB II (1).pdf - Published Version Restricted to Repository staff only Download (480kB) | Request a copy
	Text (Bab 3) BAB III.pdf - Published Version Restricted to Repository staff only Download (294kB) | Request a copy
	Text (Bab 4) BAB IV.pdf - Published Version Restricted to Repository staff only Download (595kB) | Request a copy
	Text (Bab 5 v) BAB V.pdf - Published Version Restricted to Repository staff only Download (1MB) | Request a copy

Abstract

ABSTRAK Perlakuan panas pada baja mempunyai peranan penting dalam upaya mendapatkan sifat – sifat tertentu yang diinginkan sesuai kebutuhan. Dalam penelitian ini meliputi proses pemanasan baja karbon menengah (HQ 760) pada temperature 830°C, 840°C, dan 850°C dilanjutkan dengan pendinginan cepat didalam oli. Untuk menunjang penelitian tersebut akan diamati struktur mikro. Dari hasil penelitian diperoleh bahwa nilai kekerasan tertinggi terjadi pada benda uji yang mengalami perlakuan panas pada temperatur 830°C yaitu sebesar 95,5 HRB dibandingkan dengan nilai kekerasan benda uji tanpa perlakuan (asli) sebesar 90,3 HRB. Hal ini akibat terjadi perubahan sruktur pearlite menjadi martensite. Kata Kunci: Baja karbon menengah, perlakuan panas, hardening

Item Type:	Thesis (S-1)
Subjects:	T Technology > TJ Mechanical engineering and machinery
Divisions:	Fakultas Teknik > S1 Teknik Mesin
Depositing User:	Tn Aldi Viyoga
Date Deposited:	05 May 2021 03:42
Last Modified:	05 May 2021 03:42
URI:	http://repository.univ-tridinanti.ac.id/id/eprint/2625

Actions (login required)

View Item